Transient dynamic response and failure of composite structure under cyclic loading with fluid structure interaction
Teo, Hui Fen
Didoszak, Jarema M.
MetadataShow full item record
With the growing interest in using composites in naval shipbuilding, it is crucial to understand the behavior of structures, especially the Fluid Structural Interaction (FSI) aspect of the composites under dynamic loading, to ensure the survivability of the platform at sea. The objective of this study is to perform displacement-controlled fatigue cyclic loading on quasi-isotropic E-glass laminate, which is commonly used in the shipbuilding industry. The fatigue cyclic loading is performed in both air and water environments with varied frequencies to analyze the structural behavior and failure pattern of composites under FSI. The results of the experiment show significant FSI effects on the fatigue failure life cycle of the composite under high frequency loading of 2 Hz, 5 Hz and 10 Hz. The degree of FSI effect of the 5 Hz and 10 Hz cyclic loading is significantly higher than 2 Hz cyclic loading and the FSI effect varies for 5 Hz and 10 Hz, with 5 Hz loading exhibiting a higher impact on the composite. The knowledge gained from the investigation will benefit ongoing research into understanding the dynamic response and failure mechanism of the composite structures under FSI. The insights and suggestions for follow-on studies will contribute to the development of future life prediction modeling or tools that will help to prevent premature failures in the design of composite vessel—particularly a naval ship—where survivability is vital.
RightsThis publication is a work of the U.S. Government as defined in Title 17, United States Code, Section 101. Copyright protection is not available for this work in the United States.
Showing items related by title, author, creator and subject.
Kwon, Y.W.; Panick, C.J. (Springer, 2020);Recently, a set of failure criteria based on a multiscale model was developed for fibrous composites. Those criteria used stresses and strains occurring in the fiber and matrix material level. The failure criteria consisted ...
Yang, Shih-Ting (Monterey, California. Naval Postgraduate School, 1994-06);This study investigates the failure modes, failure strengths, and failure criteria of laminated composite plates with stress concentration and subjected to bending loading. Graphite/epoxy composites ...
Boey, Yew Khuan (Monterey, California. Naval Postgraduate School, 2011-12);This study investigated the progressive damage/failure of composite panels with open circular holes under progressive axial loading. A series of experiments was carried out to determine the failure in laminated specimens ...